Suprachrome
Non-Precious Alloys
| Color | WHITE |
| Type | 5 |
| ADA Class | Cobalt BASE (CPB) |
|
Application
|
|
| Processing | |
|---|---|
| Investment | PARTIAL |
| Crucible | Quartz or Zircon |
| Degassing Temp C | 650-1010 |
| Oxidation Procedure |
| Solder & Laser Wires | |
|---|---|
| PreSolder | WELDING RODS |
| PostSolder | ELECTRO WELD |
| Laser Wire | LWNPCO |
| Physical Properties | |
|---|---|
| VHN After Firing | |
| VHN Soft | |
| VHN Hard | 410 |
| Proof Stress Soft MPa | |
| Proof Stress Hard MPa | 600 |
| Tensile Strength Soft MPa | |
| Tensile Strength Hard MPa | |
| Elongation Soft | |
| Elongation Hard | 9 |
| Elastic Modulus GPa | 200 |
| Composition | |
|---|---|
| Chromium (Cr) | 28.5 |
| Cobalt (Co) | 63.4 |
| Molybdenum (Mo) | 6.0 |
| Silicon (Si) | 0.8 |
| Manganese (Mn) | 0.8 |
| Iron (Fe) | 0.5 |
| Thermal Properties | |
|---|---|
| Melting Range C | 1300-1370 |
| Casting Temp C | 1510 |
| Density g/cc | 8.3 |
| Expansion at 500C | |
| Expansion at 600C | |
| Burnout Temp C | 1095 |